MATERIAL TESTING
Abrasion/Salt Spray
The main function is to use specified Grinding Wheel with specified Load to rub
the surface of specimen, and after a setup number of timer of abrasive, evaluate
the following conditions of the surface after test, and ratio the endurance
characteristic of abrasion for this material.
●
Worn out condition
●
The loss of the weight
●
The loss of the physical volume
●
The thickness that been worn out, etc.
●
Use NBS standard gum to ratio the
endurance characteristic of abrasion for this material.
Specification:
●
Machine Dimension: 33 ×43 ×30cm
●
Machine Weight: 30 kg
●
Power Supply:
240V 50Hz
●
Rotary Speed: 60RPM (Or to be specified)
●
Counter: LCD
display, 6Digit (Optional Setting), Auto-Brake
●
Load (Weights) : 250g, 500g,
QC-619T, Abrasion Tester
MSS-B, Salt Spray Testers
Testing Chamber: It is made of P.V.C. sheet, its internal structure uses advance
technical of stainless steel pipe. The feature is well-reinforced, temperature
well kept, and deformed free and keep temperature stable
●
Heat-up method of
chamber is “5 direction heat-up method”, able to control constant temperature
inside chamber (± 1°C)
●
Saturated air tank: The heating air purpose saturated
air tank for mist spraying is made of stainless steel SUS 304, its feature with
press-resistant, water-leakage free, air-leakage free, and deformed free, This
installation also included auto-deleted when over pressure, to ensure a longer
life span
●
Heating constant temperature installation: It using 5-directions
heating up by water type to control temp. Ensure temperature kept and
constantly. It is also help to prevent the Choppy temperature- Electricity
saving for long period use
●
Specimen placement: The specimen angle is
15°/30°. Place them average ready to test, standard specimen size is 150
Accessories:
1) Air compressor: 1Set. 2) Testing purpose pharmaceutical products: NaCl (Sodium chloride),
NaOH(sodium hydroxide), CuCl (copper (I) chloride), and CH3COOH (glacial acetic acid) each one bottle. Adjust appliances:
Litmus paper, spoon, straw, and concoct tank for each
●
The main difference between the above stated types are the testing
chamber’s capacity. Other functions are the same
●
The industrial standard request the testing capacity reached 0.43m3 or
above. Selecting proper type according to consumer’s specimen size requirement.
Model
MSS-A
MSS-B
Internal Dim. (cm)
W60xD40xH45
W90xD50xH60
External Dim. (cm)
W125xD106xH94
W155xD120xH105
Quantity of collecting cup
1PC
2PC
Power of heater (Watt)
1000W
2000W
Temp. range
Chamber
Room temp. ~50°C
Air
Room temp. ~63°C
Features
Temp. constancy
±0.5°C
Saturated air pressure (kg/cm2)
0.8~2.0 ±0.01
Spray volume (ml/80cm2/hr)
0.5~0.3
PH-salt spray test
6.5~7.2
PH-CASS test
3.0~3.2
Material
Exterior
P.V.C or P.P
Interior
P.V.C or P.P
System
Salt spray vehicle
Air+acid (base) liquid
Heating
SUS#316 Stainless steel heater+Teflon coating
Control
Digital electronic control
Power source
AC 1Ø, 220V ±10%, 50/60Hz
QC-619T
MSS-B
1000g (Free assorting by user)
●
Grinding Wheel specification: (As customer specifies)
●
The cleft between Grinding Wheel
and Specimen Plate-Holder: 37 ~ 38mm
●
Grinding Wheel: Diameter 2”, thickness 1/2”
●
Pitch of Left and Right Grinding
Wheel: 63.5mm
●
Specimen size: Ø100mm, center hole: Ø8mm, thickness: 0.5~3mm (Adjustable), available for soft/hard
material
●
Accessories: Vacuum cleaner 1Set, Specimen cutter 1Pc (A), Wrench 1Pc (K), Grind Wheel 1Set (B), Sand Paper
5Pcs (C)
●
Attachment: Warranty Certificate, Instruction Manual each one piece.
x70mm or 100 x 65mm, finished-products test directly is also available. It is use glass-made nozzle and conformed to
Bernoulli theorem to make salt a mist shape & fallen mist capacity is adjustable. (Generally use 1-2cc/hour)
Usage:
Salt
spray tester is used for testing rust-proof treatment of material, such as metal surface that after painting, coating,
electroplating, anodizing, films of organic and non-organic…etc. It’s a corrosion and Rust-Resistant test. It is for checking the
corrosion-resistant of products (specimen) under long time corrosion after treatment like anodize, rustproof oil, chemical, etc.